Apparatus for multistage thermal treatment of rubber waste, in particular scrap tires

ABSTRACT

A process for multistage thermal treatment of rubber waste, in particular scrap tires, is proposed. The process comprises several steps of transferring a product granulate of rubber waste into three different sequencing heating zones of a reactor ( 10 ). In the heating zones ( 11   a,    11   b,    11   c ) the product granulate is heated at a first temperature between 100° to 200° C., preferably 150° to 180° C., then at a second temperature between 200° to 350° C. and at a third temperature between 300° to 600° C. The temperature is maintained until such time that no further oil is emitted within the respective heating zone. As a final step, the product granulate is removed from the reactor ( 10 ) and the desirable solid materials are separated.

BACKGROUND OF THE INVENTION

The present invention concerns a process and an apparatus for the reclaiming of desirable materials from rubber waste, in particular scrap tires.

Approximately 3.2 million tons of scrap tires arise per year in the European Union. In the past most scrap tires were deposited in landfills. Since the year 2003 an EU Guideline has prohibited the dumping of scrap tires. Currently, scrap tires are burnt as boiler fuel in particular in the cement industry. Other used vehicle tires are recycled to be used in pavements.

Pyrolysis of scrap tires has also been known for many years. By pyrolysis which is carried out in the absence of oxygen at above 500° C. and which is an endothermic process the scrap tires are decomposed. Thus, substantial amounts of carbon black, steel, oil and gas can be recovered from the scrap tires. However, the pyrolysis processes for scrap has failed to become widely established in particular due to the low quality of the pyrolysis products which do not satisfy the commercial requirements.

In EP 1 163 092 81 a pyrolysis process for scrap tires is disclosed in which a pyrolysis chamber with three heating zones comprising different temperatures is provided. The scrap tires are fed as granulate to the pyrolysis chamber comprising different heating zones. The pyrolysis chamber is rotated with respect to the flight to transport the granulated tire pieces. A first heating zone of the pyrolysis chamber has a temperature between 700° to 800° C. A second heating zone of the pyrolysis chamber has a second temperature between 600° to 700° C. A third heating zone has a temperature between 500° to 600° C.

In U.S. Pat. No. 6,835,861 82 a low energy method of pyrolysis of rubber material is disclosed. The rubber material is inserted together with a clay catalyst into an pyrolysis apparatus with three different heating phases in a first embodiment. In the first phase, called activation phase, the rubber material is heated to temperature between 68.3° to 287.8° C. In the second phase the reaction temperature is held between 287.8° C. and 454.4° C. In the third phase the temperature is held at the same level by heating. In a second embodiment, which is also disclosed in U.S. Pat. No. 6,833,485 B2 and U.S. Pat. No. 7,341,646 B2 the rubber material is transported through three different zones, each zone comprising a 20 temperature of preferably about 287.8° C. In both processes the catalyst is not removed after conclusion of the pyrolysis.

As mentioned above, one problem in the known processes for scrap tires is that the quality of the carbon black recovered is outside the commercial specifications for carbon black due to the either too high or too low temperature of the processes. Therefore the recovered carbon black is of only limited commercial use.

Consequently, it is one object of the present invention to provide a thermal treatment process and an apparatus for thermal treatment of rubber waste, in particular scrap tires, which provide recovered material of such high purity that it can be commercially used.

SUMMARY OF THE INVENTION

The present invention suggests a process for multistage thermal treatment of rubber waste, in particular scrap tires, comprising the following steps:

-   -   transferring a product granulate of the rubber waste from a         supply into a pyrolysis reactor;     -   heating the product granulate at a first temperature between         100° to 200° C., preferably 150° to 180° C., in a first heating         zone of the reactor so long until light oils are no longer         emitted;     -   transferring the product granulate from the first to a second         heating zone in the reactor;     -   heating the product granulate at a second temperature between         200° to 20 300° C. in a second heating zone of the reactor so         long until medium heavy oils are no longer emitted;     -   transferring the product granulate from the second to a third         heating zone in the reactor;     -   heating the product granulate at a third temperature between         300° to 600° C., preferably between 400° and 550° C., in a third         heating zone so long until heavy oils are no longer emitted;     -   removing the product granulate from the pyrolysis reactor and         separating the desirable solid materials.         wherein the process is carried out within a low pressure         environment.

In the first heating zone a depolymerization of the rubber waste takes place. This process is different from the known pyrolysis processes.

The applicant has found that a slow and long-lasting thermal treatment process in the first heating zone at low temperature has the effect that the light oils do not form non-removable products which contaminate the carbon black. This also applies to the other steps carried out in the other heating zones of the reactor. Pyrolysis is only carried out in the third heating zone, where all possible contaminants are already removed, which results in the carbon black received after the third heating zone having a very high purity. In addition, the carbon black has a large surface which results in high adsorption properties. Owing to its special structure, the recovered carbon black floats on water. Therefore, the carbon black received after the third heating zone can be used as adsorption material in particular for the adsorption of oils and lipids.

Further developments in line with claim 1 are referred to in the dependent claims.

The multistage thermal treatment process is carried out within a low pressure environment in which the pressure is advantageously between 20 to 50 mbar.

The process is carried out in each heating zone very slowly for a time period between 2 to 4 hours. Such a slow thermal treatment process prevents the formation of non-removable products which contaminate the desirable materials.

According to one preferred embodiment, the carbon black recovered after the third heating zone is refined at high temperatures for a time period of about 2 hours. The carbon black received after the refining process has a very high percentage of purity comparable with commercial grade carbon black. Therefore, the carbon black recovered can be commercially used. In particular, the carbon black recovered can be used again in industrial production.

It is advantageous that the product granulate be moved slowly within and through the reactor.

According to one preferred embodiment, the product is moved by means of a conveyor screw.

The reactor is filled to about 60% of its volume.

A cleaning step can be carried out for about 2 hours at high temperatures without further feeding of the product.

According to a further aspect, the present invention also relates to an apparatus for multistage thermal treatment of rubber waste, in particular scrap tires, having a reactor comprising:

-   -   a first heating zone which can be heated to a first temperature         between 25 100° to 200° C., preferably 150° to 180° C.;     -   a second heating zone which can be heated to a second         temperature between 200° to 300° C. and     -   a third heating zone which can be heated to a temperature         between 300° C. to 600° C., preferably between 400° to 550° C.,         and     -   a conveyor means which transports the product granulate within         and through the reactor.

Accordingly, the product granulate is transported by means of the conveyor means through the different heating zones of the reactor.

According to one preferred embodiment the conveyor means is a driven conveyor screw.

In order to provide different speeds within the reactor, the conveyor screw can comprise worms of different pitch.

According to one preferred embodiment, the conveyor screw comprises recesses in which rollers are located to prevent depositing of the product.

It is further advantageous that the rollers should be staggered in the circumferential direction of the conveyor screw.

According to a further embodiment, the conveyor screw comprises at its outer circumference supports made of non-ferrous metal to support the inner wall of the reactor.

It is further advantageous that the reactor comprises a housing which is reinforced in the regions of the non-ferrous supports of the conveyor screw.

It is advantageous, that in the reinforced region of the reactor a reduced temperature should prevail. This causes condensation of oils within the reactor whereby the conveyor screw is lubricated in the region of the non-ferrous supports.

According to one preferred embodiment the reactor comprises an upper portion in which a vapour exhaust is provided. During the thermal treatment process the vapour exhaust takes up gases and oils recovered from the product granulate by means of the process according to the invention.

According to one preferred embodiment the vapour exhaust comprises an annular pipe which is connected to a condenser.

It is further advantageous that a cleaning means is provided within the vapour exhaust.

According to one preferred embodiment the cleaning means is an annular driven chain on which a brush or brush elements are arranged.

According to a further embodiment the housing of the reactor comprises a longitudinal groove with a perforated sheet at the vapour exhaust in which the cleaning means is guided.

It is advantageous that the perforated sheet comprises longitudinal slots. These brush elements of the cleaning means are able to clean the annular pipe properly by gearing into the longitudinal slots.

An outlet conveyor screw is arranged at the outlet of the reactor. The conveyor screw conveys the pyrolysed product granulate from the reactor.

In another feature of the invention heating mats for heating the heating zones are arranged at the outside of the housing of the reactor.

Other features and advantages of the present invention will become apparent from the following more detailed description of the embodiments, which describe, by way of example, the principles of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a schematic view of the reactor used in the multistage thermal treatment process according to the invention.

FIG. 2 shows a vertical partial section through the reactor of the apparatus according to the invention.

FIG. 3 shows a section along the lines 111-111 in FIG. 2.

FIG. 4 shows a vertical partial section through the reactor of the apparatus according to the invention.

FIG. 5 shows a vertical section along the line V-V of FIG. 4.

FIG. 6 shows a schematic view of the vapour exhaust of the reactor.

FIG. 7 shows a vertical section along the line VII-VII of FIG. 6.

FIG. 8 shows a vertical section along the line VIII-VIII of FIG. 7.

FIG. 9 is a schematic section through the granulate feeder arranged at the inlet of the reactor.

FIG. 10 is a schematic view of the separator arranged at the outlet of the reactor.

DETAILED DESCRIPTION

FIG. 1 generally illustrates the multistage thermal treatment apparatus of the present invention. The apparatus comprises a reactor 10, which has a cylindrical housing 19. Along the longitudinal axis of the reactor 10 three different heating zones 11 a, 11 b, 11 c are provided. The first heating zone 11 a can be heated to a first temperature between 100° to 200° C., preferably 150° to 180° C. The second heating zone 11 b can be heated to a second temperature between 200° to 300° C. The third heating zone 11 c can be heated to a temperature between 300° to 600° C., preferably 440° to 550° C.

The reactor 10 further comprises a conveyor screw 20 which is driven by a driving means (not shown). The conveyor screw 20 is arranged within the housing 19 of the reactor 10.

A container 14 takes up product granulate of the rubber waste, in particular scrap tires. The product granulate is transported from the container 14 to the inlet 12 of the reactor 10. The product granulate is transported within and through the reactor 10 by means of the conveyor screw 20. Accordingly, the conveyor screw 20 transports the product granulate through the heating zones 11 a, 11 b, 11 c to the outlet 13. Here, the solid product granulate in particular carbon black 16 is recovered.

The reactor 10 further comprises a vapour exhaust 15 for taking up the vapour phase of the thermally treated products. The vapour phase comprises so-called pyrolysis oil 17 and pyrolysis gas 18.

Within the reactor 10 a low pressure environment with a pressure of about 20 to 50 mbar is provided. The reactor 10 is filled to about 60% of its volume with product granulate.

Within the first heating zone 11 a, a first process is carried out for a time period of between 2 to 4 hours until light oils are emitted anymore from the product granulate. The slow and long-lasting process in the first heating zone 11 a at low temperatures has the effect that the light oils do not form non-removable products which contaminate the carbon black.

In the second heating zone 11 b the product granulate is pyrolized at a second temperature until no medium heavy oils are emitted anymore. Again, the slow and long-lasting process prevents non-removable products which contaminate the carbon black from being formed.

In the third heating zone 11 c the product granulate is pyrolized at a third temperature until no heavy oils are emitted anymore.

At the outlet 13 the product granulate is removed from the reactor 10. The desirable solid materials, in particular carbon black and steel remains, are separated.

The carbon black 16 recovered after the third heating zone 11 c has a very 20 high purity in particular if the temperature applied in the third heating zone 11 c exceeds the threshold of 500° C. In addition the carbon black 16 has a large surface resulting in high adsorption properties. Owing to its structure the carbon black 16 floats on water. Thus, the carbon black 16 received can be used as adsorption material in particular for adsorbing oils and lipids.

If a lower temperature than 500° C. was applied in the third heating zone 11 c the carbon black 16 can be refined at high temperatures of about 800° C. at low-pressure conditions for a time period of about 2 hours in order to receive commercial-grade carbon black 16 a. The carbon black recovered has a purity comparable with commercial-grade carbon black and can therefore be commercially used.

The properties of the carbon black after the refining process and after the third heating zone 11 c (T>500° C.) are listed in table I (see below).

TABLE I Properties of carbon black after refining or heating at temperatures higher than 500° C. Carbon Black Analysis Chemical Analysis/At % Carbon 95.46-96.02 Oxygen 2.38-2.90 Sodium 0.27-0.5  Magnesium 0.06-0.11 Aluminum 0.12-0.25 Silicon 0.66-1.48 Phosphorus 0.02-0.04 Sulfur 0.24-0.61 Calcium 0.29-0.93 Structure Analysis Particle size −40 nm Structure Blackberry-cluster Location for formation of pores between particles

Details of the multistage thermal treatment apparatus will now be described with reference to the drawings.

FIG. 2 shows a partial section through the reactor 10. As shown, the reactor 10 comprises a cylindrical housing 19 extending along its longitudinal axis 30. Within the housing 19 a conveyor screw 20 is arranged for conveying the product granulate within and through the reactor 10.

The conveyor screw 20 comprises a shaft 21 which is supported by means of bearings 22 at the inlet 12 and the outlet 13 of the reactor 10. The conveyor screw 20 comprises a worm 25 with a variety of pitches to provide different speeds within the reactor 10. At the outer circumference of the worm 25 non-ferrous metal supports 26 are provided in order to support the conveyor screw 20 at the inner side of the housing 19 of the reactor 10.

At the housing 19 reinforcing rings 23 are provided in the area of the supports 26.

Heating mats 24 a and 24 b are arranged at the outer circumference of the housing 19. The heating mats 24 a, 24 b can be separately controlled in order to provide different temperatures within the heating zones 11 a, 11 b, 11 c.

In the region of the reinforcing rings 23 a reduced temperature prevails. This causes a condensation of oil in the region of the supports 26 whereby the conveyors screw 20 is lubricated. The same effect occurs in the region of the supports 22.

FIG. 3 shows a vertical section along the lines III to III of FIG. 2. As shown, the non-ferrous supports 26 are supported by the housing 19 which is reinforced by the reinforcing ring 23 in this area.

Referring now to FIGS. 4 and 5, the conveyor screw 20 comprises rollers 28 arranged within the worm 25 of the conveyor screw 20. The rollers 28 prevent deposition of the product granulate on the conveyor screw 20.

As best shown in FIG. 5, the worm 25 comprises recesses 27 extending in the radial direction of the conveyor screw 20. Within each of the recesses 27 a rotating roller 28 is mounted.

FIG. 6 shows the vapour exhaust 15 of the reactor 10. The vapour exhaust 15 comprises an annular pipe 31 which is connected to a condenser 35. A cooling device (not shown) is attached to the annular pipe 31. Within the annular pipe 31 a cleaning means 32 is provided. The cleaning means 32 comprise a chain 33 which is driven by a motor 34. Brush elements 36 are arranged on the chain 33 at a distance from each other. When the cleaning means 32 is driven in the direction of arrow 37 the annular pipe 31 is cleaned. Furthermore, sprayers 38 are provided within the condenser 35 and within the annular pipe 31 for cleaning the brush elements by means of pyrolized oil.

FIG. 7 shows a vertical section along the line VII to VII of FIG. 6. The vapour exhaust 15 is located in an upper area of the reactor 10. In this region the housing 19 of the reactor 10 comprises a longitudinal groove 15 a taking up and guiding the brush elements 36 of the cleaning means 32.

FIG. 8 shows a vertical section along the line VIII to VIII of FIG. 7. A perforated sheet 15 b is arranged at the bottom of the longitudinal groove 15 a comprising a plurality of longitudinal slots 15 c. When the chain 33 is guided through the annular pipe 33 the brush elements 36 gear into these longitudinal slots 15 c and thus clean the annular pipe 31 of the vapour exhaust 15 thoroughly.

FIG. 9 shows the container 14 for the product granulate the outlet of which comprises a conveyor 39 for compressing the product granulate and conveying the same to the inlet 12 of the reactor 10. The conveyor 39 comprises a driven conveyor screw 40. The container 14 is filled with a protective gas, such as argon, to prevent oxygen from entering the conveyer 39. Thus, oxygen is prevented from coming together with the product granulate.

FIG. 9 shows the separator 42 which is arranged at the outlet 13 of the reactor 10. The product granulate is transported by means of a conveyor 41 to the separator 42. The separator 42 comprises a sedimentation basing 43. A mill 45 breaks up the product granulate into particles of about 1 to 10 μm and helps to separate the different materials. The solid materials are separated within the separator 42. The steel contained in the pyrolized product is deposited on the bottom of the sedimentation basing 43. Owing to its special structure the carbon black 26 accumulates on the surface of the water and can be removed by a stripper 44.

LIST OF REFERENCES 10 Reactor 11a First heating zone 11b Second heating zone 11c Third heating zone 12 Inlet 13 Outlet 14 Container 15 Vapor exhaust 15a Longitudinal groove 15b Perforated sheet 15c Longitudinal slots 16 Carbon black 17 Pyrolysis oil 18 Pyrolysis gas 19 Housing 20 Conveyor screw 21 Shaft 22 Bearing 23 Reinforcing ring 24 Heating mat 25 Worm 26 Support 27 Recess 28 Roller 29 Filling level 30 Longitudinal axis 31 Annular pipe 32 Cleaning means 33 Chain 34 Motor 35 Condenser 36 Brush elements 37 Arrow 38 Sprayer 39 Conveyor 40 Conveyor screw 41 Conveyor 42 Separator 43 Sedimentation basing 44 Stripper 45 Arrow 46 Arrow 

1.-8. (canceled)
 9. Apparatus for multistage thermal treatment of rubber waste, in particular scrap tires, comprising: a reactor having: a first heating zone which can be heated to a first temperature between 100° to 200° C., preferably 150° to 180° C., a second heating zone which can be heated to a first temperature between 200° to 300° C. a third heating zone which can be heated to a temperature between 300° C. to 600° C. a conveyor arranged for transporting the product granulate within and through the reactor, the reactor including an upper portion in which a vapour exhaust is provided, and a cleaner provided within the vapour exhaust.
 10. Apparatus according to claim 9, wherein the conveyor is a driven conveyor screw.
 11. Apparatus according to claim 10, wherein the conveyor screw comprises worms with different pitches to provide different speeds within the reactor.
 12. Apparatus according to claim 10, wherein the conveyor screw comprises recesses in which rollers are installed to prevent deposition of the product.
 13. Apparatus according to claim 12, wherein the rollers are staggered in the circumferential direction of the conveyor screw.
 14. Apparatus according to claim 10, wherein the conveyor screw comprises at its outer circumference supports made of nonferrous metal to support an inner wall of the reactor.
 15. Apparatus according to claim 14, wherein the reactor comprises a housing which is reinforced in an area of the non-ferrous supports of the conveyor screw.
 16. Apparatus according to claim 15, wherein in a region of the reinforcement a reduced temperature prevails.
 17. Apparatus according to claim 9 wherein the vapour exhaust includes an annular pipe connected to a condenser and sprayers are provided within at least one of the annular pipe and the condenser.
 18. Apparatus according to claim 9, wherein the vapour exhaust comprises an annular pipe which is connected to a condenser.
 19. Apparatus according to claim 9, wherein the vapour exhaust includes an annular pipe and the cleaner is provided within the annular pipe.
 20. Apparatus according to claim 9, wherein the cleaner includes an annular driven chain on which a brush or brush elements are arranged.
 21. Apparatus according to claim 15, wherein the housing of the reactor has a longitudinal groove with a perforated sheet at the vapour exhaust in which the cleaner is guided.
 22. Apparatus according to claim 21, wherein the perforated sheet comprises a plurality of longitudinal slots.
 23. Apparatus according to claim 9, wherein the reactor has an outlet at which an outlet conveyor screw is arranged.
 24. Apparatus according to claim 9, wherein heating mats for heating the heating zones are arranged at the outside of a housing of the reactor.
 25. Apparatus for multistage thermal treatment of rubber waste, in particular scrap tires, comprising: a reactor including an elongated housing having inner and outer sides and containing three different heating zones located along a longitudinal axis of the elongated housing, and a conveyer for transporting product granulate along the longitudinal axis through the three different heating zones, a vapour exhaust including a pipe that extends along the housing and is connected to each of the three different heating zones for exhausting gases and oils recovered from the product granulate from each the three different heating zones, and a cleaner including brushes that are movable along pipe for cleaning the pipe.
 26. Apparatus according to claim 25 in which the vapour exhaust includes a condenser and the pipe is an annular pipe connecting each of the three different heating zones with the condenser.
 27. Apparatus according to claim 26 in which and the brushes are arranged on an annular driven chain for moving the brushes along the annular pipe.
 28. Apparatus according to claim 26 in which a longitudinal groove is formed in an upper area of the elongated housing and a side of the pipe is connected to each of the three different heating zones through the longitudinal groove.
 29. Apparatus according to claim 28 further comprising a perforated sheet located along an interface between the longitudinal groove and the side of the pipe for guiding the brushes.
 30. Apparatus according to claim 25 in which the conveyer is a conveyer screw having an outer circumference and including supports at the outer circumference for supporting the conveyer screw at the inner side of the housing.
 31. Apparatus according to claim 30 in which an the supports comprise non-ferrous metal supports.
 32. Apparatus according to claim 30 in which the reactor further comprises first and second reinforcing rings arranged around the housing, the first reinforcing ring being located along the longitudinal axis between a first and a second of the three heating zones, the second reinforcing ring being located along the longitudinal axis between the second and a third of the three heating zones, and the supports at the outer circumference of the conveyer screw are located proximate the first and second reinforcing rings.
 33. Apparatus according to claim 32 in which the first and second reinforcing rings are located within reduced temperature zones of the reactor such that oils condensed in association with the reduced temperatures lubricate the conveyer screw proximate the supports at the outer circumference of the conveyer screw.
 34. Apparatus according to claim 25 in which the conveyer comprises a conveyer screw in the form of a worm having different pitches to provide different speeds for transporting the product granulate along the longitudinal axis within the reactor.
 35. Apparatus according to claim 25 in which the conveyer comprises a conveyer screw having recesses that extend in a radial direction and rollers that are rotatably mounted within the recesses.
 36. Apparatus according to claim 25 in which separately controlled heating mats are arranged at an outer circumference of the housing proximate to each of the three different heating zones to provide for separately controlling different temperatures within the three different heating zones such that: a first of the three heating zones can be heated to a first temperature between 100° to 200° C., preferably 150° to 180° C., a second of the three heating zones can be heated to a first temperature between 200° to 300° C. a third of the three heating zones can be heated to a temperature between 300° C. to 600° C. 